Categories |
Polymer ; Thermoplastic |
Physical Properties |
Metric |
English |
Comments |
---|---|---|---|
Density |
1.02 – 1.20 g/cc |
0.0368 – 0.0434 lb/in³ |
Average value: 1.05 g/cc Grade Count:115 |
Water Absorption |
0.250 – 1.00 % |
0.250 – 1.00 % |
Average value: 0.448 % Grade Count:24 |
Moisture Absorption at Equilibrium |
0.000 – 0.210 % |
0.000 – 0.210 % |
Average value: 0.180 % Grade Count:9 |
Water Absorption at Saturation |
0.300 – 1.03 % |
0.300 – 1.03 % |
Average value: 0.796 % Grade Count:5 |
Maximum Moisture Content |
0.0100 – 0.150 |
0.0100 – 0.150 |
Average value: 0.0256 Grade Count:9 |
Linear Mold Shrinkage |
0.00200 – 0.00800 cm/cm |
0.00200 – 0.00800 in/in |
Average value: 0.00533 cm/cm Grade Count:75 |
Linear Mold Shrinkage, Transverse |
0.00300 – 0.00800 cm/cm |
0.00300 – 0.00800 in/in |
Average value: 0.00591 cm/cm Grade Count:6 |
Melt Flow |
0.100 – 35.0 g/10 min |
0.100 – 35.0 g/10 min |
Average value: 4.94 g/10 min Grade Count:115 |
Mechanical Properties |
Metric |
English |
Comments |
Hardness, Rockwell R |
68.0 – 113 |
68.0 – 113 |
Average value: 101 Grade Count:60 |
Ball Indentation Hardness |
65.0 – 110 MPa |
9430 – 16000 psi |
Average value: 93.2 MPa Grade Count:11 |
Tensile Strength, Ultimate |
22.1 – 49.0 MPa |
3210 – 7110 psi |
Average value: 36.4 MPa Grade Count:31 |
Tensile Strength, Yield |
13.0 – 65.0 MPa |
1890 – 9430 psi |
Average value: 40.4 MPa Grade Count:112 |
|
22.1 – 59.3 MPa
|
3210 – 8600 psi
|
Average value: 40.7 MPa Grade Count:1 |
Elongation at Break |
3.00 – 150 % |
3.00 – 150 % |
Average value: 34.2 % Grade Count:71 |
Elongation at Yield |
0.620 – 30.0 % |
0.620 – 30.0 % |
Average value: 5.57 % Grade Count:49 |
Modulus of Elasticity |
1.00 – 2.65 GPa |
145 – 384 ksi |
Average value: 2.07 GPa Grade Count:57 |
|
1.50 – 2.60 GPa
|
218 – 377 ksi
|
Average value: 2.05 GPa Grade Count:1 |
Flexural Yield Strength |
0.379 – 593 MPa |
55.0 – 86000 psi |
Average value: 69.2 MPa Grade Count:73 |
|
49.6 – 113.8 MPa
|
7190 – 16510 psi
|
Average value: 81.7 MPa Grade Count:1 |
Flexural Modulus |
0.200 – 5.50 GPa |
29.0 – 798 ksi |
Average value: 2.18 GPa Grade Count:100 |
|
1.90 – 2.80 GPa
|
276 – 406 ksi
|
Average value: 2.35 GPa Grade Count:1 |
Izod Impact, Notched |
0.380 – 10.3 J/cm |
0.712 – 19.3 ft-lb/in |
Average value: 3.22 J/cm Grade Count:88 |
|
0.450 – 4.00425 J/cm
|
0.843 – 7.50160 ft-lb/in
|
Average value: 1.34 J/cm Grade Count:21 |
|
0.480 – 4.00 J/cm
|
0.899 – 7.49 ft-lb/in
|
Average value: 1.34 J/cm Grade Count:12 |
Reference : http://www.matweb.com/search/DataSheet.aspx?MatGUID=3a8afcddac864d4b8f58d40570d2e5aa&ckck=1